Mechanical reinforcement while remaining electrical insulation of glass fibre/polymer composites using core-shell CNT@SiO2 hybrids as fillers
Publication in refereed journal

香港中文大學研究人員
替代計量分析
.

其它資訊
摘要Carbon nanotubes (CNTs) have been widely used as mechanical reinforcement agents of composites. However, their aggregations, weak interfacial interaction with polymer, as well as high electrical conductivity limit their use in some especial applications. In this paper, the silicon oxide (SiO2)-coated (CNT@SiO2) core-shell hybrids with different SiO2 thickness were prepared and employed to reinforce glass fibre-reinforced bismaleimide-triazine (BT) resin (GFRBT) composites. The results indicated the mechanical properties, including tensile strength and Young's modulus increased with the increase of SiO2 thickness and CNT@SiO2 loading. Such enhanced mechanical properties were mainly attributed to the intrinsically nature of CNTs, homogeneous dispersion of the hybrids, as well as improved interfacial interaction. Meanwhile, the composites remained high electrical insulation (9.63 × 1012 Ω cm) due to the existence of SiO2 layer on CNT surface. This study will guide the design of functionalized CNTs and the construction of high-performance composites.
著者Zeng X., Yu S., Sun R., Xu J.-B.
期刊名稱Composites Part A: Applied Science and Manufacturing
出版年份2015
月份6
日期1
卷號73
出版社Pergamon Press Ltd.
出版地United Kingdom
頁次260 - 268
國際標準期刊號1359-835X
語言英式英語
關鍵詞A. Nano-structures, A. Polymer-matrix composites (PMCs), B. Electrical properties, B. Mechanical properties

上次更新時間 2021-24-01 於 02:53